Thank you. I understand that! I have no use for 20 or 40 pcs.!We discussed this last night through several emails!
Unfortunately for people like me who want 4, maybe 8 batteries, your product along with shipping cost is NOT feasible for people in the USA.Just the way it is,no fault of yours.
I would have liked to try a few. It appears you have a good battery[verrry similar to 30Q!] but at too much of a TOTAL cost for the average flashlight guy in USA!
I can get 30Q and other batteries right down the street from me w/ NO SHIPPING COST. I am grateful for that.
It is strange because the voltage tracks VTC6 pretty much identically, but it just looks like the internal resistance is a tad higher so the voltage sags a bit.
It does,but not quite as well as the others I have mentioned,the gap w/ the VTC6 has a little bigger advantage/separation on the voltage curves. While the aforementioned are basically on top of each other for 3a,5a,7a,10a and 15a. :sunglasses:
The 30Q matches very good, but the Vbatty is a bit better at end of the discharge. The VTC6 has lower internal resistance, that can be because it has been on storage for a shorter time.
I believe it is difficult to decide which one matches best.
Thanks HKJ. You inspired me to read and learn more about the other graphs you do in your review. I did notice the better “End of discharge” for the Vbatty VS. 30Q.
I do not have the understanding/knowledge you have. I am just basing what I see in the voltage curves. Now I can expand my horizons!
I am hoping Illumns or another dealer here in USA will stock them! It will be nice to do my SIMPLE run time/voltage tests on them.
I would NOT notice the output difference in my single modded throwers whether it be HG2,VTC6,30Q OR this battery. They are ALL very good batteries,it is the TYPE “A” personality that wants a little edge, regardless of how unnoticeable by eye and insignificant on paper!!! lol!
I am no authority on lithium ion cells I am just a lowly technician. However I am very curious and have been for some time now and you guys seem to be the people to answer.
Please correct me anywhere that I am wrong as I said I can fix or build anything, I am just beginning to learn how important the differences in our choice of cells really is.
With most things being pretty much equal i.e. contents of the cell itself, materials used and if it is unprotected then there is very little left that can be changed. 30q as an example only, if another company wishes to compete with that cell there are only very small variances that could even be possible. If there is no electronic control and I build a cell with the same or as close to the same materials as a 30q is manufactured from. They will appear even in tests to be the same cell.
I guess the easiest thing to ask is just how much can be changed in modern 18650 cells that could make them better?
Again please pardon my ignorance, these are the the last pieces of the puzzle that I need grow and expand my mods. My dad was a first class engineer but passed away before teaching me all I would need to know about electricity.