A DEEP carry Titanium clip on a raw Aluminum flashlight? What’s the reasoning for that one? It won’t show, and if/when it does show, it won’t match the light it’s attached to.
A titanium body? The limited spreading of the heat that this flashlight already has will be even more localised then!
Think the D4, the head and body are aluminium and have a generous material thickness, and still on turbo the heat is produced so massively that it builds up near the led-shelf without enough heat path to get it away fast enough from there.
The FW3A is built thinner than that, the time on turbo before trouble starts will be even less. Make the body titanium and you can halve even that!
A nice premium version could be made of copper, at least your turbo-time will go up a bit then. It will require a new trick to insulate the inner tube from the outer one, copper can not be simply anodised like aluminium.
The only flashlight of mine that ever actually melted parts was a FET triple in titanium. It got hot enough to melt the legs and bottoms of a carclo optic while the tail of the light was still comfortable to hold. Just a bit longer and it probably would’ve unsoldered itself. It also burned skin bad enough to leave red welts when I actually touched the head, but luckily no blisters. Titanium is beautiful and I love my ti lights, but titanium hotrods are not a good idea.