[quote=Henk4U2]

Very true Henk4U2. :+1: ā€¦. But it is worthless as it is, so on the offhand chance it might work, it wonā€™t hurt to try.

Tempering after this makeshift ā€˜heat treatingā€™ attempt might well relieve some of the brittleness.

If you do try it polarweis, let us know the outcome please.

There are 2 more SC01 in Germany.

Must be from the first batch. The clip fits tight. Seems good quality :+1:

Knurling is definitely not on the aggressive Side. The Threads are really smooth. Turning on and off works very well

IĀ“m very happy both with the Light intensity (between the low and the Mid of a Lumintop EDC01) and the Light colour

I would say the BLF Team that realized this Light and Sofirn did a very good Job :+1:

ThankĀ“s a lot for this

and Greetings from Germany

Lumintop tint doesnā€™t look too bad on these pictures either. What would you say?

both are sofirn i think.

:person_facepalming:
I thought Iā€™m expecting too much from XP-G3ā€¦

Oh, Sorry for not clarifying :blush:

Yes both are Sofirn C01, 5600K and 3200K

Here is a direct comparison with the Lumintop EDC01 on low and Med

Without direct comparison it appears to be a pure white :+1:

Doesnā€™t look too bad to be honest. One is on my way anyway but I was just wondering if Iā€™m not gonna be embarassed if I give it as a gift to someone :wink:

Thank you for the photos
The EDC01 w XP-G3 has Green Tint, and is Not High CRI, so not the same Quality of Light, as the Sofirn CO1 w Yuji

For people that want to go beyond the single mode Sofirn C01, but still with High CRI in AAA size, I highly recommend Clemenceā€™s latest offering, a High CRI 3 mode AAA light

So i threw the clip in my fireplace. The black paint was gone real fast. Waited till red hot and dipped it in olive oil(extra virgin lol). Then i tempered it by hanging it on the metal fireshield(around 200c) for 2 hours. Its much harder now but can still be bend.

I would say definitely yes, that the artifact in the Sofirn C01 is caused by the shiny cone.
.
.

My Utorch S1 Mini with shiny bezel, has a round artifact in the center of the beam, on right.

l-r 2000k E21a, 4500k N219b, 6500k XP-L

the light on the left has black magic marker on the bezel, the center light has black paint, on the right shiny
Note the three lights pictured, Utorch S1 Mini, have Aspheric Lenses, same as the Yuji LED. They are NOT supposed to have a hotspot.

conclusion
Shiny bezel causes hotspot artifacts in Sofirn C01 :wink:

Thatā€™s good info polarweis, thank you. :+1:
You said you went to ā€œred hotā€ & got some results.
When mine get here I think I am going to try going a bit hotter, into the ā€˜Orange hotā€™ range; temper a bit hotter too & see what happens.
It would sure help if we knew what metal the clip was made of.
ā€¦ā€¦.
Edit: It would seem to indicate, since you were able to achieve some degree of hardness; it is not ā€˜mild steelā€™ at least.

[quote=polarweis]

Perhaps not quite as throwy as the initial GT, but thanks for indulging my curiosity about how it would look with that big reflector. :smiley:

[quote=teacher
[/quote]
Thatā€™s good info polarweis, thank you. :+1:
You said you went to ā€œred hotā€ & got some results.
When mine get here I think I am going to try going a bit hotter, into the ā€˜Orange hotā€™ range; temper a bit hotter too & see what happens.
It would sure help if we knew what metal the clip was made of.
ā€¦ā€¦.
Edit: It would seem to indicate, since you were able to achieve some degree of hardness; it is not ā€˜mild steelā€™ at least.
[/quote]

Yeah i think with more heat it will get a little bit harder. It will get a strange blue color tho.

They say its hot enough when its not magnetic any more. Mine was still magnetic. I think you really need a torch to get enough heat.

Yep, you are correct about the ā€œnot magneticā€. :+1:

A torch will work just fine or a ā€˜heat treat ovenā€™ if one has access to it. Fortunately I do.

It will be a ā€˜crap shootā€™ getting it right on this unknown metalā€¦ but if we can figure it out by trial & errorā€¦ we can share it for anyone interested.

The info you shared is a great startā€¦ :+1:

Just want to say that I received mine 3 days ago. I bought it 10th November, so it took 32 days to get to the UK. I like the 5600K tint alot, it's the best cool tint I've seen so far. Great job to everyone who was involved to get this light into production!

Thanks John, good to know. I ordered mine a day after you, so hopefully theyā€™ll be here soon!

Mine are in US last week, but damn, once in ISC cutoms in New York OR Chicagoā€¦.it can be another 2 weeks to get to me in southern USā€¦.Iā€™m used to it after so many years, so Iā€™ve learned to just wait and wait and waitā€¦ā€¦. :innocent: :smiling_imp: :person_facepalming:

When I saw the top picture, I first thought it looked like that itty bitty animal theyā€™ve found that apparently canā€™t be killed! Facepalm

Perhaps this is good info who receives a C01 with bending clip that does not have any springiness to it.

Btw, I managed to convince Sofirn that their clips are faulty, they admit that the heating process was wrong and they sent what is left of the batch back to the manufacturer for improvement.

Inspired by polarweiss I tried his method of hardening the clip, warmed up to orange, quencing in vegetable oil, keeping it at 200 degrees for 2 hours. Nothing happened, fail, no springiness at all was achieved.

Then I did not care about the clip becoming brittle anymore, blowtorched it to almost yellow, next to the fast running tap, and while orange/yellow dunked it under the stream and presto: perfect springiness without being too brittle it seems sofar.

I videoā€™ed it: